ALASM=ASM Specialty Handbook Aluminum and Alloys CSNDT=CSNDT compiled by Eddy Current Technology Incorporated ECTM=Eddy Current Testing Manual on Eddy Current Method compiled by Eddy Current Technology Incorporated NDT Mag=NDT Magazine Sept/Oct 1955, Cosgrove Article compiled by Eddy Current Technology Incorporated Material Conductivity Resistivity Reference Notes (% IACS) (Siemens/m) (Ohm-m) (See Endnotes) Aluminum Pure 61 3.54E+07 2.83E-08 ECTM 99.99% 64.94 3.77E+07 2.66E-08 CSNDT 99.99% 64.94 [...]
ALASM=ASM Specialty Handbook Aluminium und Aluminiumlegierungen
CSNDT=CSNDT zusammengestellt von Eddy Current Technology Incorporated
ECTM=Eddy Current Testing Manual on Eddy Current Method zusammengestellt von Eddy Current Technology Incorporated NDT Mag=NDT Magazine Sept/Oct 1955, Cosgrove Artikel zusammengestellt von Eddy Current Technology Incorporated
Material | Leitfähigkeit | Widerstandsfähigkeit | Referenz | Anmerkungen | |
(% IACS) | (Siemens/m) | (Ohm-m) | (Siehe Endnoten) | ||
Aluminium | |||||
Reines | 61 | 3.54E+07 | 2.83E-08 | ECTM | |
99.99% | 64.94 | 3.77E+07 | 2.66E-08 | CSNDT | |
99.99% | 64.94 | 3.77E+07 | 2.66E-08 | ALASM | |
Red X-8 Cond. Entlastet | 29 | 1.68E+07 | 5.95E-08 | CSNDT | |
Rot X-8 als Guss | 26 | 1.51E+07 | 6.63E-08 | CSNDT | |
11S Bedingung. T3 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
13 | 39 | 2.26E+07 | 4.42E-08 | CSNDT | |
14S Bedingung. "0" | 50 | 2.90E+07 | 3.45E-08 | CSNDT | |
14S Zustand. T6 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
17S Bedingung. "0" | 45 | 2.61E+07 | 3.83E-08 | CSNDT | |
17S Zustand. T4 | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
18S Bedingung. "0" | 50 | 2.90E+07 | 3.45E-08 | CSNDT | |
18S Bedingung. T61 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
2S Bedingung. "0" | 59 | 3.42E+07 | 2.92E-08 | CSNDT | |
2S Kond. H18 | 57 | 3.31E+07 | 3.03E-08 | CSNDT | |
24S Bedingung. "0" | 50 | 2.90E+07 | 3.45E-08 | CSNDT | |
24S Zustand. T4 | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
24S Zustand. T6 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
3S Zustand. "0" | 50 | 2.90E+07 | 3.45E-08 | CSNDT | |
3S Kond. H 12 | 42 | 2.44E+07 | 4.11E-08 | CSNDT | |
3S Kond. H 14 | 41 | 2.38E+07 | 4.21E-08 | CSNDT | |
3S Kond. H 18 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
32S Bedingung. "0" | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
32S Zustand. T6 | 35 | 2.03E+07 | 4.93E-08 | CSNDT | |
40E | 35 | 2.03E+07 | 4.93E-08 | CSNDT | |
43 (geglüht) | 42 | 2.44E+07 | 4.11E-08 | CSNDT | |
43 als Besetzung | 37 | 2.15E+07 | 4.66E-08 | CSNDT | |
A51S Zustand. "0" | 55 | 3.19E+07 | 3.14E-08 | CSNDT | |
A51S Bedingung. T4 und T6 | 45 | 2.61E+07 | 3.83E-08 | CSNDT | |
52S Bedingung. "0" und H 38 | 35 | 2.03E+07 | 4.93E-08 | CSNDT | |
53S Zustand. "0" | 45 | 2.61E+07 | 3.83E-08 | CSNDT | |
53S Bedingung. T4 und T6 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
56S Bedingung. "0" | 29 | 1.68E+07 | 5.95E-08 | CSNDT | |
56S Zustand. H 38 | 27 | 1.57E+07 | 6.39E-08 | CSNDT | |
61S Bedingung. "0" | 45 | 2.61E+07 | 3.83E-08 | CSNDT | |
61S Bedingung. T4 und T6 | 40 | 2.32E+07 | 4.31E-08 | CSNDT | |
75S Zustand. T6 | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
85 | 28 | 1.62E+07 | 6.16E-08 | CSNDT | |
Aluminium Allcast | |||||
Als Besetzung | 27 | 1.57E+07 | 6.39E-08 | CSNDT | |
Kond. Sol. H.T. & Stress entlastet | 36 | 2.09E+07 | 4.79E-08 | CSNDT | |
Sol H.T. und Aged | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
Stressabbau | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
Aluminiumlegierung (geschmiedet) | |||||
1050-0 | 61.3 | 2.81E-08 | ALASM | ||
1060-O | 62 | 2.78E-08 | ALASM | ||
1060-H18 | 61 | 2.78E-08 | ALASM | ||
1100 | 57.00 - 61.80 | 3.45E+07 | 2.90E-08 | NDT-Magazin | |
1100-O | 59 | 2.92E-08 | ALASM | ||
1100-H18 | 57 | 3.02E-08 | ALASM | ||
1145-O | 61 | 2.83E-08 | ALASM | ||
1145-H18 | 60 | 2.83E-08 | ALASM | ||
1199-O | 64.5 | 2.67E-08 | ALASM | ||
1350-O | 61.8 | 2.79E-08 | ALASM | ||
1350-Hx | 61 | 2.82E-08 | ALASM | ||
2011-T3 | 36.00 - 36.50 | 2.10E+07 | 4.76E-08 | NDT-Magazin | |
2011-T3 und T4 | 39 | 4.40E-08 | ALASM | ||
2011-T8 | 45 | 3.80E-08 | ALASM | ||
2014-F und -0 | 48.60 - 50.70 | 2.88E+07 | 3.47E-08 | NDT-Magazin | |
2014-O | 50 | 3.40E-08 | ALASM | ||
2014-T3 und -T4 | 32.50 - 34.80 | 1.95E+07 | 5.12E-08 | NDT-Magazin | |
2014-T3, T4 und T451 | 34 | 5.10E-08 | ALASM | ||
2014-T6 | 38.00 - 39.70 | 2.25E+07 | 4.44E-08 | NDT-Magazin | |
2014-T6, T651und T652 | 40 | 4.30E-08 | ALASM | ||
2017-F | 49.30 - 49.50 | 2.87E+07 | 3.49E-08 | NDT-Magazin | |
2017-O | 50 | 3.50E-08 | ALASM | ||
2017-T4 | 34 | 5.00E-08 | ALASM | ||
2024-F | 46.80 - 48.50 | 2.76E+07 | 3.62E-08 | NDT-Magazin | |
2024-O | 50 | 3.40E-08 | ALASM | ||
2024-T3 | 28.60 - 36.10 | 1.88E+07 | 5.33E-08 | NDT-Magazin | |
2024-T36 | 29.10 - 29.50 | 1.70E+07 | 5.88E-08 | NDT-Magazin | |
2024-T3, T36, T351, T361 und T4 | 30 | 5.70E-08 | ALASM | ||
2024-T4 | 28.80 - 31.00 | 1.73E+07 | 5.77E-08 | NDT-Magazin | |
2024-T6, T81, T851 und T861 | 38 | 4.50E-08 | ALASM | ||
2036-O | 52 | 3.32E-08 | ALASM | ||
2036-T4 | 41 | 4.21E-08 | ALASM | ||
2048-T851 | 42 | 4.00E-08 | ALASM | ||
2124-O | 50 | 3.45E-08 | ALASM | ||
2124-T851 | 39 | 4.42E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
2127-T4 | 42.10 - 42.40 | 2.45E+07 | 4.08E-08 | NDT-Magazin | |
2218-T61 | 37.4 | 2.17E+07 | 4.61E-08 | NDT-Magazin | |
2218-T61 | 38 | 4.50E-08 | ALASM | ||
2218-T72 | 40 | 4.30E-08 | ALASM | ||
2219-O | 44 | 3.90E-08 | ALASM | ||
2219-T31, T37 und T351 | 28 | 6.20E-08 | ALASM | ||
2219-T62, T81, T87 und T851 | 30 | 5.70E-08 | ALASM | ||
2319-O | 44 | 3.90E-08 | ALASM | ||
2618 | 40.2 | 2.33E+07 | 4.29E-08 | NDT-Magazin | |
2618-T61 | 37 | 4.70E-08 | ALASM | ||
3003-O | 44.70 - 49.80 | 2.74E+07 | 3.65E-08 | NDT-Magazin | |
3003-O | 50 | 3.40E-08 | ALASM | ||
3003-H14 und -H12 | 37.80 - 51.50 | 2.59E+07 | 3.86E-08 | NDT-Magazin | |
3003-H12 | 42 | 4.10E-08 | ALASM | ||
3003-H14 | 41 | 4.20E-08 | ALASM | ||
3003-H18 | 40 | 4.30E-08 | ALASM | ||
3003-H24 und -H28 | 37.80 - 47.50 | 2.47E+07 | 4.04E-08 | NDT-Magazin | |
3004 | 39.40 - 43.50 | 2.40E+07 | 4.16E-08 | NDT-Magazin | |
3004-O | 42 | 4.10E-08 | ALASM | ||
X3005-O | 50.10 - 50.30 | 2.91E+07 | 3.44E-08 | NDT-Magazin | |
3105-O | 45 | 3.83E-08 | ALASM | ||
4032-O | 40 | 4.31E-08 | ALASM | ||
4032-T6 | 35.30 - 36.30 | 2.08E+07 | 4.82E-08 | NDT-Magazin | |
4032-T6 | 36 | 4.79E-08 | ALASM | ||
4043-F | 52.30 - 54.30 | 3.09E+07 | 3.24E-08 | NDT-Magazin | |
4043-O | 42 | 4.10E-08 | ALASM | ||
5005 | 52.30 - 52.80 | 3.05E+07 | 3.28E-08 | NDT-Magazin | |
5005-O und H38 | 52 | 3.32E-08 | ALASM | ||
5050 | 48.30 - 49.80 | 2.85E+07 | 3.52E-08 | NDT-Magazin | |
5050-O und H38 | 50 | 3.40E-08 | ALASM | ||
5052 | 33.60 - 37.60 | 2.07E+07 | 4.84E-08 | NDT-Magazin | |
5052-O und H38 | 35 | 4.93E-08 | ALASM | ||
5056 | 28.10 - 29.80 | 1.68E+07 | 5.96E-08 | NDT-Magazin | |
5056-O | 29 | 5.90E-08 | ALASM | ||
5056-H38 | 27 | 6.40E-08 | ALASM | ||
5083 | 29 | 5.95E-08 | ALASM | ||
5086 | 31 | 5.60E-08 | ALASM | ||
5154 | 30.50 - 32.80 | 1.84E+07 | 5.45E-08 | NDT-Magazin | |
5154 | 32 | 5.39E-08 | ALASM | ||
5182 | 31 | 5.56E-08 | ALASM | ||
5252 | 35 | 4.90E-08 | ALASM | ||
5254 | 32 | 5.40E-08 | ALASM | ||
5356-O | 29 | 5.94E-08 | ALASM | ||
5357 | 42.30 - 47.00 | 2.59E+07 | 3.86E-08 | NDT-Magazin | |
5454 | 34 | 5.10E-08 | ALASM | ||
5456 | 29 | 5.95E-08 | ALASM | ||
5457 | 46 | 3.75E-08 | ALASM | ||
5652 | 35 | 4.90E-08 | ALASM | ||
5657 | 54 | 3.20E-08 | ALASM | ||
6005-T5 | 49 | 3.50E-08 | ALASM | ||
6009-O | 54 | 3.19E-08 | ALASM | ||
6009-T4 | 44 | 3.92E-08 | ALASM | ||
6009-T6 | 47 | 3.67E-08 | ALASM | ||
6010-O | 53 | 3.25E-08 | ALASM | ||
6010-T4 | 39 | 4.42E-08 | ALASM | ||
6010-T6 | 44 | 3.92E-08 | ALASM | ||
6053 | 39.30 - 48.00 | 2.53E+07 | 3.95E-08 | NDT-Magazin | |
6061-F und -0 | 42.30 - 48.50 | 2.63E+07 | 3.80E-08 | NDT-Magazin | |
6061-O | 47 | 3.70E-08 | ALASM | ||
6061-T4 | 37.60 - 40.50 | 2.27E+07 | 4.42E-08 | NDT-Magazin | |
6061-T4 | 40 | 4.30E-08 | ALASM | ||
6061-T6 und -T9 | 40.00 - 44.80 | 2.46E+07 | 4.07E-08 | NDT-Magazin | |
6061-T6 | 43 | 4.00E-08 | ALASM | ||
6062-F | 47.00 - 51.00 | 2.84E+07 | 3.52E-08 | NDT-Magazin | |
6062-T4 | 43.50 - 44.00 | 2.54E+07 | 3.94E-08 | NDT-Magazin | |
6062-T6 | 44.70 - 49.50 | 2.73E+07 | 3.66E-08 | NDT-Magazin | |
6063-O | 58 | 3.00E-08 | ALASM | ||
6063-T1 | 50 | 3.50E-08 | ALASM | ||
6063-T5 | 55 | 3.20E-08 | ALASM | ||
6063-T6 und T83 | 53 | 3.30E-08 | ALASM | ||
6066-O | 40 | 4.30E-08 | ALASM | ||
6066-T6 | 37 | 4.70E-08 | ALASM | ||
6070-T6 | 44 | 3.90E-08 | ALASM | ||
6101-T6 | 57 | 3.02E-08 | ALASM | ||
6101-T61 | 59 | 2.92E-08 | ALASM | ||
6101-T63 | 58 | 2.97E-08 | ALASM | ||
6101-T64 | 60 | 2.87E-08 | ALASM | ||
6101-T65 | 58 | 2.97E-08 | ALASM | ||
6151-0 | 53.30 - 55.00 | 3.14E+07 | 3.18E-08 | NDT-Magazin | |
6151-O | 54 | 3.20E-08 | ALASM | ||
6151-T4 | 41.50 - 43.30 | 2.46E+07 | 4.07E-08 | NDT-Magazin | |
6151-T6 | 42 | 4.10E-08 | ALASM | ||
6151-T6 | 43.90 - 45.00 | 2.58E+07 | 3.88E-08 | NDT-Magazin | |
6151-T6 | 45 | 3.80E-08 | ALASM | ||
6201-T81 | 54 | 3.20E-08 | ALASM | ||
6205-T1 | 45 | 3.70E-08 | ALASM | ||
6205-T5 | 49 | 3.50E-08 | ALASM | ||
6262-T9 | 44 | 3.90E-08 | ALASM | ||
6351-T6 | 46 | 3.80E-08 | ALASM | ||
6463-T1 | 50 | 3.40E-08 | ALASM | ||
6463-T5 | 55 | 3.10E-08 | ALASM | ||
6463-T6 | 53 | 3.30E-08 | ALASM | ||
6951-F | 53.00 - 53.10 | 3.08E+07 | 3.25E-08 | NDT-Magazin | |
6951-0 | 55.70 - 56.50 | 3.25E+07 | 3.07E-08 | NDT-Magazin | |
7005-O | 43 | 4.01E-08 | ALASM | ||
7005-T53, T5351, T63 und T6351 | 38 | 4.54E-08 | ALASM | ||
7005-T6 | 35 | 4.93E-08 | ALASM | ||
7039 | 32-40 | 4.3E-8-5.4E-8 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
7049 | 40 | 4.30E-08 | ALASM | ||
7050-O | 47 | 3.67E-08 | ALASM | ||
7050-T76 und T7651 | 39.5 | 4.36E-08 | ALASM | ||
7050-T736 und T73651 | 40.5 | 4.26E-08 | ALASM | ||
7072 | 60.00 - 60.10 | 3.48E+07 | 2.87E-08 | NDT-Magazin | |
7072-O | 60 | 2.87E-08 | ALASM | ||
7075-F | 44.50 - 47.80 | 2.68E+07 | 3.74E-08 | NDT-Magazin | |
7075-T6 | 31.40 - 34.80 | 1.92E+07 | 5.21E-08 | NDT-Magazin | |
7075-T6 | 32 | 1.86E+07 | 5.39E-08 | ECTM | |
7075-W | 27.00 - 37.00 | 1.86E+07 | 5.39E-08 | NDT-Magazin | |
7075-T6, T62, T651 und T652 | 33 | 5.22E-08 | ALASM | ||
7075-T76 und T7651 | 38.5 | 4.48E-08 | ALASM | ||
7075-T73, T7351 und T7352 | 40 | 4.31E-08 | ALASM | ||
7076 | 35 | 3.75E-08 | ALASM | ||
7175-O | 46 | 3.75E-08 | ALASM | ||
7175-T66 | 36 | 4.79E-08 | ALASM | ||
7175-T736 und T73652 | 40 | 4.31E-08 | ALASM | ||
7178-O | 46 | 3.75E-08 | ALASM | ||
7178-T6 und T651 | 32 | 5.39E-08 | ALASM | ||
7178-T76 und T7651 | 39 | 4.42E-08 | ALASM | ||
X7178-F und -0 | 45.50 - 46.00 | 2.65E+07 | 3.77E-08 | NDT-Magazin | |
X7178-W und T6 | 26.80 - 32.60 | 1.72E+07 | 5.81E-08 | NDT-Magazin | |
7475-O | 46 | 3.75E-08 | ALASM | ||
7475-T61 und T651 | 36 | 4.79E-08 | ALASM | ||
7475-T761 und T7651 | 40 | 4.31E-08 | ALASM | ||
7475-T7351 | 42 | 4.11E-08 | ALASM | ||
Aluminium-Legierungen (Guss) | |||||
122 Perm. Form wie gegossen | 34 | 1.97E+07 | 5.07E-08 | CSNDT | |
122 Sand Cond. T2 | 41 | 2.38E+07 | 4.21E-08 | CSNDT | |
122 Sand Besch. T61 | 33 | 1.91E+07 | 5.23E-08 | CSNDT | |
113 | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
C113 | 27 | 1.57E+07 | 6.39E-08 | CSNDT | |
A 132 Beschaffenheit. T551 | 29 | 1.68E+07 | 5.95E-08 | CSNDT | |
201.0-T6 | 27-32 | 4.5E-8-6.4E-8 | ALASM | ||
206.0-T6 | 27-32 | 5.4E-8-6.4E-8 | ALASM | Leitfähigkeit umgerechnet von Widerstand- | |
206.0-T7 | 32-34 | 5.0E-8-5.4E-8 | ALASM | Leitfähigkeit umgerechnet von Widerstand- | |
208,0 wie gegossen | 31 | 5.56E-08 | ALASM | ||
(208.0) 108 | 31 | 1.80E+07 | 5.56E-08 | CSNDT | |
208,0 geglüht | 38 | 4.54E-08 | ALASM | ||
214 | 35 | 2.03E+07 | 4.93E-08 | CSNDT | |
A214 | 33 | 1.91E+07 | 5.23E-08 | CSNDT | |
218 | 24 | 1.39E+07 | 7.18E-08 | CSNDT | |
220 | 21 | 1.22E+07 | 8.21E-08 | CSNDT | |
242.0-T21, Sand | 44 | 3.92E-08 | ALASM | ||
(242,0) 142 Sand Cond. T21 | 44 | 2.55E+07 | 3.92E-08 | CSNDT | |
242.0-T571, Sand | 34 | 5.07E-08 | ALASM | ||
(242,0) 142 Sand Besch. T571 | 34 | 1.97E+07 | 5.07E-08 | CSNDT | |
242.0-T77, Sand | 38 | 4.54E-08 | ALASM | ||
(242,0) 142 Sand Besch. T77 | 37 | 2.15E+07 | 4.66E-08 | CSNDT | |
242.0-T61, Dauerform | 33 | 5.22E-08 | ALASM | ||
295.0-T4 | 35 | 4.93E-08 | ALASM | ||
(295,0) 195 Zustand. T4 | 35 | 2.03E+07 | 4.93E-08 | CSNDT | |
295.0-T62 | 37 | 4.93E-08 | ALASM | ||
(295,0) 195 Bedingt. T62 | 37 | 2.15E+07 | 4.66E-08 | CSNDT | |
296.0-T4 und T6 | 33 | 5.22E-08 | ALASM | ||
(296,0) B 195 Bedingung. T4 | 35 | 2.03E+07 | 4.93E-08 | CSNDT | |
(296,0) B 195 Bedingung. T6 | 36 | 2.09E+07 | 4.79E-08 | CSNDT | |
308 | 37 | 4.66E-08 | ALASM | ||
(308.0) A 108 | 37 | 2.15E+07 | 4.66E-08 | CSNDT | |
R 317 | 30 | 1.74E+07 | 5.75E-08 | CSNDT | |
319 | 27 | 6.39E-08 | ALASM | ||
319 Sand | 27 | 1.57E+07 | 6.39E-08 | CSNDT | |
319 Perm. Form | 28 | 1.62E+07 | 6.16E-08 | CSNDT | |
336.0-T551 | 29 | 5.95E-08 | ALASM | ||
355.0-T51, Sand | 43 | 4.01E-08 | ALASM | ||
355 Sand Cond. T51 | 43 | 2.49E+07 | 4.01E-08 | CSNDT | |
355.0-T6, Sand | 36 | 4.79E-08 | ALASM | ||
355 Sand Kond. T6 | 36 | 2.09E+07 | 4.79E-08 | CSNDT | |
355.0-T61, Sand | 39 | 4.42E-08 | ALASM | ||
355 Sand Beschaffenheit. T61 | 37 | 2.15E+07 | 4.66E-08 | CSNDT | |
355.0-T7, Sand | 42 | 4.10E-08 | ALASM | ||
355 Sand Kond. T7 | 42 | 2.44E+07 | 4.11E-08 | CSNDT | |
355.0-T6, Dauerform | 39 | 4.42E-08 | ALASM | ||
355 Zul. Form Kond. T6 | 39 | 2.26E+07 | 4.42E-08 | CSNDT | |
356.0-T51, Sand | 43 | 4.01E-08 | ALASM | ||
356 Sand Cond. T51 | 43 | 2.49E+07 | 4.01E-08 | CSNDT | |
356.0-T6, Sand | 39 | 4.42E-08 | ALASM | ||
356 Sand Kond. T6 | 39 | 2.26E+07 | 4.42E-08 | CSNDT | |
356.0-T7, Sand | 40 | 4.31E-08 | ALASM | ||
356.0-T6, Dauerform | 41 | 4.21E-08 | ALASM | ||
360 | 28 | 6.16E-08 | ALASM | ||
A360.0 | 30 | 5.75E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
360 | 37 | 2.15E+07 | 4.66E-08 | CSNDT | |
380 | 27 | 6.50E-08 | ALASM | ||
380 | 27 | 1.57E+07 | 6.39E-08 | CSNDT | |
383 | 23 | 7.50E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
384 | 22 | 7.84E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
A384.0 | 23 | 7.50E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
390.0-F | 27 | 6.39E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
390.0-T5 | 25 | 6.90E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
413 | 31 | 5.56E-08 | ALASM | ||
443,0 Nach Guss | 37 | 4.66E-08 | ALASM | ||
443,0 Geglüht | 42.05 | 4.10E-08 | ALASM | Leitfähigkeit umgerechnet von Widerstand- | |
514 | 35 | 4.93E-08 | ALASM | ||
518 | 25 | 6.90E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
520.0-T4 | 21 | 8.21E-08 | ALASM | ||
535 | 20 | 7.50E-08 | ALASM | ||
712 | 35 | 4.93E-08 | ALASM | ||
713 | 35 | 4.93E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
750 | 45 | 2.61E+07 | 3.83E-08 | CSNDT | |
771 | 27 | 6.39E-08 | ALASM | Widerstand umgerechnet von Leitfähigkeit- | |
850 | 47 | 3.67E-08 | ALASM |
Als Gründer von MachineMFG habe ich mehr als ein Jahrzehnt meiner Karriere der metallverarbeitenden Industrie gewidmet. Meine umfangreiche Erfahrung hat es mir ermöglicht, ein Experte auf den Gebieten der Blechverarbeitung, der maschinellen Bearbeitung, des Maschinenbaus und der Werkzeugmaschinen für Metalle zu werden. Ich denke, lese und schreibe ständig über diese Themen und bin stets bestrebt, in meinem Bereich an vorderster Front zu bleiben. Lassen Sie mein Wissen und meine Erfahrung zu einem Gewinn für Ihr Unternehmen werden.